Effect of temperature on the corrosion inhibition on mild steel in 2.0M H2SO by some organic compounds containing S and N atoms in absence and presence of halides
تاثير درجة الحراره على تثبيط تاكل الصلب فى 2.0 مولار حمض الكبريتيك باستحدام مركبات تحتوى على ذرات S and N. فى غياب ووجود الهاليدات
 
Subject : Scientific Research 
Document Language : English 
Abstract : The corrosion rate of mild steel in 2.0M H2SO4 containing 10% EtOH in absence and presence 0.1M halides was studied by both hydrogen evolution and mass loss methods. The obtained results showed that the rate of corrosion was increased with the increase of temperature. The activation parameters for mild steel corrosion in 2.0M H2SO4 in absence and presence 0.1 M Cl-& Br- in the corrosive medium leads to a decrease in the ∆Eapp,& ∆H± and ∆S± values than that of acid solutions which means that these ions becomes more effective as the temperature increases and corrosion inhibition is found . The studied compounds are found to accelerate the corrosion of mild steel at 20°C then at 30°C the inhibition of corrosion is increased then a decrease in the inhibition of corrosion or acceleration at 50 to 60°C in compounds A, B and C is found, which indicates that these compounds are physically adsorbed on the mild steel surface and it also indicated that the inhibited film formed on the metal surface most probably destroyed with faster rates at high temperatures. Corrosion inhibition by studied compounds in presence 0.1M Cl- or Br at different temperatures shows that corrosion of mild steel largely decreases with rising temperature this was explained to be that the halides are chemically adsorbed on steel surface and a co-adsorption of the studied compounds (A-C) is occurred. 
ISSN : 1012-1319 
Journal Name : Science Journal 
Volume : 24 
Issue Number : 2 
Publishing Year : 1329 AH
2008 AD 
Article Type : Article 
Added Date : Tuesday, July 24, 2012 

Researchers

Researcher Name (Arabic)Researcher Name (English)Researcher TypeDr GradeEmail
سناء طاهر عربArab, Sanaa TaherInvestigatorDoctoratedr.s.arab@hotmail.com
سعيدة رويض المحياويAl-Mhyawi, Saida RewiredResearcherDoctoratesraszyad@hotmail.com

Files

File NameTypeDescription
 34020.pdf pdfملخص البحث
 36925.pdf pdfScientific Research

Back To Researches Page